Neovascularization effect of biodegradable gelatin microspheres incorporating basic fibroblast growth factor

Biodegradable microspheres were prepared through glutaraldehyde cross-linking of gelatin without using any surfactants as a carrier matrix of basic fibroblast growth factor (bFGF). In the in vitro system, bFGF was sorbed to microspheres of acidic gelatin with an isoelectric point (IEP) of 5.0, but not to those of basic gelatin with an IEP of 9.0. The rate of bFGF sorption to the acidic gelatin microsphere in phosphate-buffered saline solution (pH 7.4) was smaller than that in water. Following incorporation of bFGF into the microspheres at 4 degrees C for 12 h, bFGF release from the bFGF-incorporating microspheres was studied. Approximately 30% of incorporated bFGF was released from the acidic gelatin microsphere within the initial 3 h, followed by no substantial release, whereas the basic gelatin microsphere released almost completely the incorporated bFGF within 1 day. It is likely that when basic bFGF molecules were immobilized to the acidic gelatin constituting microspheres through polyion complexation, they were not readily released under the in vitro nondegradation condition of gelatin. Incorporation of anionic carboxylmethyl cellulose (CMC) into the acidic gelatin microspheres reduced the amount of bFGF desorbed initially. This indicates that the initial burst is ascribed to free bFGF which is not ionically interacted with the acidic gelatin. CMC will function as a bFGF sorbent to suppress the initial leakage from the microspheres. When injected subcutaneously into the mouse back, bFGF-incorporating acidic gelatin microspheres were degraded over time and induced neovascularization around the injection site, in marked contrast to bFGF in the solution form. CMC incorporation slowed down the biodegradation and vascularization effect of bFGF-incorporating gelatin microspheres. It was concluded that the gelatin microsphere was a promising carrier matrix of bFGF to enhance the vascularization effect.