The formation and interpretation of defect images from crystalline materials in a scanning transmission electron...

The technique of scanning transmission electron microscopy (STEM) has been employed usefully in studies of amorphous materials, and the theory of image formation and interpretation in this case has been well developed. Less attention has been given to the practical and theoretical problems associated with the use of STEM for the examination of crystalline materials. In this case the contrast mechanisms are dominated by Bragg diffraction and so they are quite different from those occurring in amorphous substances. In this paper practical techniques for the observation and interpretation of contrast from defects in crystalline materials are discussed. It is shown that whilst images of defects are obtained readily under all typical STEM operating conditions, the form of the image and the information it contains varies with the angle subtended at the specimen by the detector. If this angle is too large significant image modifications relative to the "conventional" transmission electron microscope case may occur and the resolution of the image may degrade. If this angle is too small, then signal to noise considerations make an interpretation of the image difficult. In this paper we indicate how the detector angle may be chosen correctly, and also present techniques for setting up a STEM instrument for imaging a crystalline material containing lattice defects.