Material properties of cobweb silk from the black widow spider Latrodectus hesperus

We present the material analysis of scaffolding silk from the cobweb of the black widow spider Latrodectus hesperus. 30 strands were tested from the webs of nine spiders. Strands were stretched at 0.211 mm/s as force and extension were recorded. Cross-sectional area was measured under 1000 x oil-immersion light microscopy. The stress strain curve shows that cobweb silk is a distinct material from other known spider silks. The average breaking point for this cobweb silk is 1.1 +/- 0.5 GPa at 0.22 +/- 0.05 strain. All samples increased stiffness as they were stretched, but to different extents. Variation in stiffness might be due to differential crystallization or alignment of the silk proteins during stretching.