Effect of water storage on the silanization in porcelain repair strength

This study examined the long-term water storage affect of silanization on shear bond strength of composite resin to porcelain. One hundred and sixty square-shaped specimens were fabricated and sanded flat sequentially with silicone carbide papers. The specimens were then placed into four groups and 16 subgroups of 10 specimens each randomly. Four commercially available silane systems, two one-mix and two two-mix, were tested in this study. Teflon tubes with an internal diameter of 2.97 mm and 2 mm in height were filled with a dual cure composite resin (Mirage FLC), placed on the silanated surfaces and light-cured for 120 s. Specimens were stored in room temperature water and subjected to shear bond strength testing after 24 h, 1 week, 1 month and 3 month periods of immersion. An Instron Universal testing machine with a crosshead speed of 0.5 mm/min was used for the testing. The mean values of the shear bond strengths ranged from 4.38 MPa (24-h period) to 23.90 MPa (3-month period). ANOVA and Scheffe' tests were used to analyse data with confidence level at 95%. All groups recorded an increase in bond strength after one week as compared with the 24-h period (P<0.05). With the exception of a one-mix system, all systems showed significantly higher bond strength at 3 weeks as compared with the 24-h and 1-week water storage periods. In conclusion, bond strength of composite resin to porcelain resulting from silanization of porcelain increased during the experimental period. The bond strength also varied for different silanes used in this study.