Ultrasonic deposition of high-selectivity nanoporous carbon membranes
1DuPont Central Research and Development, Experimental Station, Wilmington, DE 19880, USA. Center for Catalytic Science and Technology, Department of Chemical Engineering, University of Delaware, Newark, DE 19716, USA.
Abstract:
Ultrasonic deposition creates a thin film of polymer on a tubular, macroporous, stainless steel support. Using polyfurfuryl alcohol as the nanoporous carbon precursor and a pyrolysis temperature of 723 kelvin, a membrane was prepared with the following permeances, measured in moles per square meter per Pascal per second: nitrogen, 1.8 x 10(-12); oxygen, 5.6 x 10(-11); helium, 3.3 x 10(-10); and hydrogen, 6.1 x 10(-10). The ideal separation factors as compared to that for nitrogen are 30:1, 178:1, and 331:1 for oxygen, helium, and hydrogen, respectively.