Thermal decomposition and reconstitution of hydroxyapatite in air atmosphere

In this paper, the decomposition and reconstruction behavior of hydroxyapatite (HAP) during heating and cooling in air atmosphere were studied. The commercial HAP were chosen and gradually heated to 1500 degrees C and cooled to room temperature by a program controlled SiC heated furnace. X-ray diffraction (XRD) and Fourier-transformed infrared (FTIR) analysis were used to investigate the change of crystalline phases and functional groups of HAP at different temperatures. Weight change of samples was recorded by thermogravimetric analysis (TGA) during heating and cooling. The results revealed that HAP gradually releases its OH- ions and transforms into OHAP in the temperature of 1000-1360 degrees C. Above 1360 degrees C, the OHAP would decompose into TTCP and alpha TCP phase. The OH- stretching bands of HAP could be traced by FTIR even at the temperature of 1350 degrees C which indicates HAP decomposition. HAP does not dehydrate completely before decomposition. We speculated that some oxyapatite (OAP) might be formed during dehydration with a great amount of OHAP still left in the system even up to the temperature of decomposition. In the temperature range of 1400-1500 degrees C, there was no significant difference in XRD patterns, only TTCP and alpha TCP crystalline phases were observed. When the HAP gradually cools from 1500 degrees C, a part of TTCP and alpha TCP would directly reconstruct into OAP around 1350 degrees C. OAP existed in the temperature range of 1350-1300 degrees C during cooling. When the temperature decreased to 1290 degrees C, a part of TTCP and alpha TCP reconstructed into OHAP by rehydration reaction and OAP were rehydrated into OHAP as well. At 1100 degrees C, the rest of TTCP and alpha TCP reconstitutes into HAP. As the temperature decreases, the OHAP is gradually rehydrated and reconstituted into HAP.