Preparations and properties of a novel grafted segmented polyurethane-bearing glucose groups

Novel grafted polyurethane-bearing glucose groups were synthesized through a graft copolymerization of a prefabricated polyurethane containing poly(butadiene) glycol (PBD) and hydrogenated poly(butadiene) glycol (HPBD) soft segments, and 4,4'-methylenediphenyl diisocyanate (MDI) hard segment with a hydrophilic monomer glycosylethyl methacrylate (GEMA) in solution in the presence of 2,2'-azobis(isobutyronitrile) (AIBN) as an initiator. The bulk characteristics of the grafted polyurethanes were investigated by infra-red (IR) spectroscopy and gel permeation chromatography (GPC) measurements. The glucose groups were oriented on the surface of the cast film of grafted polyurethane with different graft-on percentages as revealed by electron spectroscopy for chemical analysis (ESCA), attenuated total reflectance infra-red spectroscopy (ATR-FTIR), and water contact angle. The grafted polyurethane surfaces which showed decreased water contact angles also indicate that hydrophilic glucose groups are present at the surface. The hemocompatibilities of these polymer surfaces were evaluated by platelet-rich plasma (PRP) contacting tests. It was found that the surface of grafted polyurethane with a graft-on percentage of 23.4% showed a good hemocompatibility in terms of platelet adhesion and shape variation. It indicates that glucose groups on the surface are effective for the improvement of hydrophilicity as well as hemocompatibility.