Effect of protein on the dissolution of HA coatings

The dissolution behavior of hydroxyapatite (HA) in the presence and absence of protein needs to be investigated in order to fully understand the initial cellular response to HA surfaces. In this study, HA coatings were characterized using X-ray diffraction, X-ray photoelectron spectroscopy, and Fourier transform infrared spectroscopy (FTIR) prior to protein study. Fibronectin and albumin adsorption study were also performed. Calcium and phosphorus released in the presence and absence of albumin were measured. pH of the solution was measured daily. From the materials characterization, it was observed that the coatings exhibit a HA-type structure, with traces of sodium on the surface. FTIR indicated the possible presence of carbonates on the coatings. From the adsorption study, the amount of albumin adsorbed (0.052+/-0.005 microg/mm2) was statistically higher than the amount of fibronectin adsorbed on HA surfaces (0.035+/-0.002 microg/mm2). Flame atomic absorption indicated a significantly higher calcium ions released initially for HA coatings incubated with proteins as compared to coatings in the absence of proteins. However, after 7 days incubation, no significant difference in calcium ions release was observed between the HA coatings in the presence and absence of proteins. Phosphorus dissolution on HA coatings was not significantly affected by the presence of proteins. Thus, it was suggested from this study that the initial dissolution properties of calcium ions from HA coatings was dependent on the media.