[On the polymerization of pour type resin (author's transl)]

The initial polymerization point and the polymerization progress have been observed on powder-liquid pour type acrylic resin and one-liquid pour type acrylic resin. The results are as follows: 1. In case of un-heating at the bottom of powder liquid resin, in the former stage the polymerization makes the regular progress from the bottom part to the upper of the mould, but in the latter stage it does some irregular one. In case of heating at the bottom, at first it shows a better regular progress as in the case of un-heating. 2. In case of un-heating at the bottom of one-liquid resin, in the first stage the polymerization makes the regular progress from the bottom part of the resin and at the same time from its middle of the mould, and then to the upper part and the sprue part. In case of heating at the bottom, it begins just from the heated part, then it goes quite regularly to the middle, the upper, and the sprue part, and lastly the polymerization shrinkage concentrates exclusively at the sprue part.