Two-body wear resistance and degree of conversion of laboratory-processed composite materials
L A Knobloch1, R E Kerby, R Seghi
1Section of Restorative Dentistry, Prosthodontics and Endodontics, Ohio State University College of Dentistry, Columbus, USA. knobloch.3@osu.edu
Purpose:
The purpose of this investigation was to evaluate the relative 2-body abrasive wear and degree of conversion of 4 laboratory-processed composites (Targis, Concept, belleGlass, and Artglass) and 2 direct placement composites (Herculite and Heliomolar) after 7 days of storage.
Materials And Methods:
Human enamel was used as a positive control for 2-body abrasive wear, and 10 cylindric specimens (3.5-mm diameter, 8-mm height) of each material were prepared and stored in distilled water at 37 +/- 2 degrees C for wear testing. Relative 2-body abrasive wear rates were determined using a 30-micron diamond disk and a 2-body pin-on-disk apparatus. Subsequently, 3 polymerized specimens that had been stored in sealed polyethylene vials for 7 days were prepared for degree of conversion testing. The degree of conversion was determined on an infrared spectrometer using standard baseline techniques and various internal standards.
Results:
Statistical analysis using analysis of variance and the Tukey-Kramer multiple range test indicated significant differences between several of the materials tested for both 2-body abrasive wear and degree of conversion.
Conclusion:
Concept exhibited significantly less 2-body abrasive wear compared to the direct and indirect composites (P < 0.01). Concept and belleGlass exhibited a mean degree of conversion that was significantly higher than any of the other composites tested (P < 0.01).