The behaviour of Al in MSW incinerator fly ash during thermal treatment

Fly ash from municipal solid waste (MSW) incinerators contains leachable metals, including potentially hazardous heavy metals. The metal content of the fly ash can be reduced by thermal treatment, which vaporizes the volatile metal compounds. After heat treatment of fly ash at 1000 degrees C for 3 h, less metal was able to be leached from the thermally treated ash than from the ash without thermal treatment. Al and Cr were the exceptions. These metals were more soluble in the ash that had been thermally treated. This paper focuses on the leaching behaviour of Al only. Both simple and sequential extraction leaching tests showed that the leachable Al for the heat-treated fly ash is about twice that of the untreated fly ash. The sequential test further revealed that (i) the majority of the leachable Al is associated with Fe-Mn oxides in the fly ash, and (ii) most of the unleachable Al resides in the silicate matrices of the heat-treated and untreated fly ash. Pure chemicals, Al(2)O(3), CaO and CaCl(2), simulating the relevant ingredients in the fly ash, were used for studying their reactions at 1000 degrees C. The aluminum compounds were identified by X-ray Diffraction (XRD). Two new chemical phases produced by the thermal treatment were identified; Ca(AlO(2))(2) and 12CaO.7Al(2)O(3). Their formation suggests a mechanism whereby thermal treatment of fly ash would produce more soluble Al.