The mechanical properties of fresh and cryopreserved arterial homografts
F Pukacki1, T Jankowski, M Gabriel
1Department of General and Vascular Surgery, Medical Academy of Poznan, Poland.
Objectives:
To assess the effect of cryopreservation on the elasticity and compliance of arterial allografts.
Materials And Methods:
Iliofemoral segments of arteries and veins harvested from multiorgan donors were divided into two groups: fresh-control, tested for 24 hours after harvesting, and cryopreserved in liquid nitrogen after pretreatment with 20% dimethylsulphoxide and stored for an average time of 22 days. Vessel wall elastic properties were evaluated from the stress-strain relationship in a specially designed test cell fixed to the Instron Universal Testing Machine.
Results:
The elastic modulus of the artery control group (1.54+/-0.33 MPa, n=20) was not significantly different from the cryopreserved group (1.69+/-0.61 MPa, n=15). Similarly, values for unfrozen veins (3.11+/-0.65 MPa, n=47) were not significantly different from those of frozen samples (2.71+/-0.85 MPa, n=38). Control compliance (6. 86+/-1.79x10(-5)%/Pa, for arteries; 3.84+/-0.81x10(-5)%/Pa, for veins) was similar to that of the cryopreserved group (6.66+/-1. 80x10(-5)%/Pa, for arteries; 4.16+/-1.21x10(-5)%/Pa, for veins).
Conclusions:
Cryopreservation maintains the important elastic properties of arterial and venous allografts during average storage time of 22 days.