Quantification of the Relationship between Porosity and Interparticle Forces for the Packing of Wet Uniform Spheres

Feng1, Yu

  • 1School of Materials Science and Engineering, The University of New South Wales, Sydney, NSW, 2052, Australia

Journal of Colloid and Interface Science
|November 18, 2000
PubMed

More Related Videos

Surface Properties of Synthesized Nanoporous Carbon and Silica Matrices09:31

Surface Properties of Synthesized Nanoporous Carbon and Silica Matrices

Published on: March 27, 2019

Determining Surface Areas and Pore Volumes of Metal-Organic Frameworks06:45

Determining Surface Areas and Pore Volumes of Metal-Organic Frameworks

Published on: March 8, 2024

Related Concept Videos

Intermolecular Forces and Physical Properties02:56

Intermolecular Forces and Physical Properties

Van der Waals Equation01:10

Van der Waals Equation

The ideal gas law is an approximation that works well at high temperatures and low pressures. The van der Waals equation of state (named after the Dutch physicist Johannes van der Waals, 1837−1923) improves it by considering two factors.
First, the attractive forces between molecules, which are stronger at higher densities and reduce the pressure, are considered by adding to the pressure a term equal to the square of the molar density multiplied by a positive coefficient a. Second, the volume...
The Van der Waals Equation01:26

The Van der Waals Equation

The ideal gas law is based on two simplifying assumptions: first, that there are no intermolecular attractions between gas molecules, and second, that the volume occupied by the molecules themselves is negligible compared with the volume of the container. However, these assumptions don't hold up under all conditions - specifically, at high pressures and low temperatures, as gas tends to deviate from ideal gas behavior.The van der Waals equation is an enhanced version of the ideal gas law,...
Porosity and Absorption of Aggregate01:20

Porosity and Absorption of Aggregate

Aggregates contain pores of varying sizes; while some are completely enclosed within the particles, others open onto the surface, allowing water to penetrate. The porosity of aggregates is a major factor contributing to the overall porosity of concrete, given that aggregates constitute about three-quarters of concrete's volume.
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the aggregate...
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...
Pore Size Distribution01:23

Pore Size Distribution

In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
Adequate...