Viscoplasticity and the dynamics of brittle fracture

I propose a model of fracture in which the curvature of the crack tip is a relevant dynamical variable and crack advance is governed solely by plastic deformation of the material near the tip. This model is based on a rate-and-state theory of plasticity introduced in earlier papers by Falk, Lobkovsky, and myself. In the approximate analysis developed here, fracture is brittle whenever the plastic yield stress is nonzero. The tip curvature finds a stable steady-state value at all loading strengths, and the tip stress remains at or near the plastic yield stress. The crack speed grows linearly with the square of the effective stress intensity factor above a threshold that depends on the surface tension. This result provides a possible answer to the fundamental question of how breaking stresses are transmitted through plastic zones near crack tips.