Drug release kinetics from polymeric films containing propranolol hydrochloride for transdermal use

Polymeric films containing propranolol hydrochloride (PPN) were formulated and evaluated with a view to select a suitable formulation for the development of transdermal drug delivery systems. Films containing different ratios of ethyl cellulose (EC), poly(vinylpyrrolidone) (PVP), and PPN were prepared by mercury substrate method. In vitro drug release and skin permeation studies were conducted using paddle over disk and modified Franz diffusion cell, respectively. The drug release profiles from the polymeric film indicated that the drug content in the film decreased at an apparent first-order rate, whereas the quantity of drug release was proportional to the square root of time. The release rate of PPN increased linearly with increasing drug concentration and PVP fraction in the film, but was found to be independent of film thickness. The increase in release rate may be due to leaching of hydrophilic fraction of the film former, which resulted in the formation of pores. It was also observed that the release of drug from the films followed the diffusion-controlled model at low drug concentration. A burst effect was observed initially, however, at high drug loading level, which may be due to rapid dissolution of the surface drug followed by the diffusion of the drug through the polymer network in the film. The in vitro skin permeation profiles displayed increased flux values with increase of initial drug concentration in the film, and also with the PVP content. From this study, it is concluded that the films composed of EC/PVP/PPN, 9:1:3, 8:2:2, and 8:2:3, should be selected for the development of transdermal drug delivery systems using a suitable adhesive layer and backing membrane for potential therapeutic applications.