Electrolytic A12O3 coating on co-cr-mo implant alloys of hip prosthesis

The ceramic films over metallic implant surfaces have the potential to improve implant performance with respect to implant fixation, wear, or corrosion. In this study, the electrolytic Al2O3 coatings on F-1537 Co-Cr-Mo alloy were conducted in an aqueous solution of Al(NO3)3. Through the cycle polarization test in Hank's solution, it was found that the corrosion potential and protection potential of the alumina-coated were higher than that of the uncoated, and the corrosion current density was lower. The phase transformation of A12O3 film on Co-Cr-Mo alloy annealed at 800 K revealed todlite (5Al2O3 . H2O) and thetaAl2O3 (113) preferred orientation for 20 min, and thetaAl2O3 (200) preferred orientation with eta phase for 80 min. Scanning electron microscopy/energy dispersive spectroscopy observations after the scratch tests showed that the adhesion of the alumina films on Co-Cr-Mo alloy can load a stress over the yield strength (450 MPa) of Co-Cr-Mo alloy. The wear loss of ultra-high molecular-weight polyethylene to the Al2O3-coated specimen was eight times less than that to the uncoated. It is concluded that such Al2O3-coated films on Co-Cr-Mo implant alloy exhibit excellent quality in corrosion, adhesion, and wear for the application of hip prosthesis.