Microleakage of light-cured resin and resin-modified glass-ionomer dentin bonding agents applied with co-cure vs...

This in vitro study evaluated the effect of dentin bonding agents in reducing microleakage after three months in Class V restorations restored with Z100 resin composite. Materials tested were three types of resin-based dentin bonding agents: a multi-step (Scotchbond Multi-Purpose); a one-step (Scotchbond One-Step); a self-etching, self-priming (Clearfil Liner Bond) and a resin-modified glass ionomer (GC Fuji Bond LC). Class V cavity preparations with occlusal margins in enamel and gingival margins in cementum were prepared both on labial and lingual surfaces of extracted premolar teeth. Restorations (two per tooth) were distributed randomly into nine test groups (n = 10) consisting of the various DBAs applied with co-cure and pre-cure techniques, and no dentin bonding as a negative control group. Samples were stored in saline for three months, thermocycled, stained with silver nitrate, then sectioned through the middle of the preparation to facilitate the removal of the composite resin restoration. For groups treated with the pre-cure technique, the differences between the enamel leakage values of SBMP-control, CFLB-control and SB1S-control subgroups were significant (p < 0.05). For enamel leakage values of groups treated with the co-cure technique, the differences between the SBMP-control, SB1S-control, CFLB-control and Fuji LC-control subgroups were significant (p < 0.05). For cementum leakage values of groups treated with pre-cure technique, the difference between the CFLB-control and the Fuji, SBMP and SB1S groups was significant (p < 0.05). No significant differences could be detected between the cementum leakage values of groups treated with the co-cure technique (p > 0.05). The differences between the values obtained with application of CFLB with the pre-cure and co-cure techniques at the cementum margins were found to be statistically significant (p = 0.02). No statistically significant differences could be detected between the pre-cure and co-cure values of the other test materials. Generally for every group, cementum microleakage values were greater than enamel microleakage values (p < 0.05). The use of Scotchbond Multi-Purpose, Scotchbond One-Step and Fuji Bond LC with the co-cure technique to decrease the application time did not cause any significant increase in microleakage. Only pre-curing using Clearfil Liner Bond provided better microleakage properties than the other pre-cured adhesives.