Related Experiment Video
Updated: Aug 10, 2026
08:26
Development of Amelogenin-chitosan Hydrogel for In Vitro Enamel Regrowth with a Dense Interface
Published on: July 10, 2014
Strength of a 'no-bottle' adhesive system bonded to enamel and dentine
Dental Update
|February 24, 2001
Abstract:
Existing bonding systems permit effective bonding to enamel or dentine. Bonding to dentine is mainly achieved through the hybridization of dentine with resin. However, despite their success, the 'three-bottle' systems do have drawbacks--the large number of steps involved may be confusing and prone to errors of application, as well as being time consuming. Recently developed systems have significantly reduced the number of steps and the total treatment time, but deliver a reliable outcome.
More Related Videos
Related Concept Videos
01:22EDTA: Chemistry and Properties
Polydentate ligands are most widely used in complexometric titrations because they form more stable complexes with the metal ions than mono- or bidentate ligands due to the chelate effect. Examples of polydentate ligands are ethylenediaminetetraacetic acid (EDTA), crown ethers, and cryptands. The most important feature of optimal polydentate ligands is the ability to form 1:1 complexes in a single-step process. Amino carboxylic acid derivatives are frequently used as complexing agents. EDTA is...
01:17Mortar Properties
Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to the...
01:20Strength of Cement
Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
01:12Bonding and Strength of Aggregate
The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...