Surface roughness and wettability of enamel and dentine surfaces prepared with different dental burs

The aim of dental adhesive restorations is to produce a long lasting union between the restoration and the tooth structure. This bond depends on many variables including the geometry of the preparation and the type of bonding agent or luting cement. It is therefore suggested that the topography of the tooth surface may influence the wettability and the bonding quality of adhesive systems. This study measured the surface roughness and wettability of enamel and dentine after preparation with different dental burs. The mesial and distal surfaces of 15 extracted sound human premolar teeth were prepared with a tungsten carbide crown bur, a diamond bur and a tungsten carbide finishing bur and finished in enamel or dentin, respectively. The prepared surfaces were analysed with a surface profilometer and scanning electron microscopy (SEM). The contact angle of distilled water on each of the prepared surfaces was used as the measure of wettability. The differences in average surface roughness (Ra) were significant between the rotary instrument groups, as revealed by a two-way ANOVA test. No differences were detected between enamel and dentine surfaces prepared with the same type of dental bur. The smoothest surfaces were those completed with tungsten carbide finishing burs. The diamond bur preparations were intermediate in the roughness assessment and the tungsten carbide crown burs gave the roughest surfaces. There were no significant differences in the contact angle measurements for the various groups. It was concluded that the surface roughness of enamel and dentine prepared by different rotary instruments had no significant influence on the wettability of distilled water on these surfaces.