Intergrowth polytypoids as modulated structures: a superspace description of the Sr(n)(Nb,Ti)(n)O(3n + 2) compound series

A new, unified superspace approach to the structural characterization of the perovskite-related Sr(n)(Nb,Ti)(n)O(3n + 2) compound series, strontium niobium/titanium oxide, is presented. To a first approximation, the structure of any member of this compound series can be described in terms of the stacking of (110)-bounded perovskite slabs, the number of atomic layers in a single perovskite slab varying systematically with composition. The various composition-dependent layer-stacking sequences can be interpreted in terms of the structural modulation of a common underlying average structure. The average interlayer separation distance is directly related to the average structure periodicity along the layer stacking direction, while an inherent modulation thereof is produced by the presence of different types of layers (particularly vacant layers) along this stacking direction. The fundamental atomic modulation is therefore occupational and can be described by means of crenel (step-like) functions which define occupational atomic domains in the superspace, similarly to what occurs for quasicrystals. While in a standard crystallographic approach, one must describe each structure (in particular the space group and cell parameters) separately for each composition, the proposed superspace model is essentially common to the whole compound series. The superspace symmetry group is unique, while the primary modulation wavevector and the width of some occupation domains vary linearly with composition. For each rational composition, the corresponding conventional three-dimensional space group can be derived from the common superspace group. The resultant possible three-dimensional space groups are in agreement with all the symmetries reported for members of the series. The symmetry-breaking phase transitions with temperature observed in many compounds can be explained in terms of a change in superspace group, again in common for the whole compound series. Inclusion of the incommensurate phases, present in many compounds of the series, lifts the analysis into a five-dimensional superspace. The various four-dimensional superspace groups reported for this incommensurate phase at different compositions are shown to be predictable from a proposed five-dimensional superspace group apparently common to the whole compound series. A comparison with the scarce number of refined structures in this system and the homologous (Nb,Ca)(6)Ti(6)O(20) compound demonstrates the suitability of the proposed formalism.