Crystal structures of synthetic 7 angstrom and 10 angstrom manganates substituted by mono- and divalent cations

The crystal structures of synthetic 7 angstrom and 10 angstrom manganates, synthetic birnessite and buserite, substituted by mono- and divalent cations were investigated by X-ray and electron diffractions. The monoclinic unit cell parameters of the subcell of lithium 7 angstrom manganate, which is one of the best ordered manganates, were obtained by computing the X-ray powder diffraction data: a = 5.152 angstroms, b = 2.845 angstroms, c = 7.196 angstroms, beta = 103.08 degrees. On the basis of the indices obtained by computing the X-ray diffraction data of Li 7 angstrom manganate, monovalent Na, K and Cs and divalent Be, Sr and Ba 7 angstrom manganates were interpreted as the same monoclinic structure with beta = 100-103 degrees as that of Li 7 angstrom manganate, from their X-ray diffraction data. In addition, divalent Mg, Ca and Ni 10 angstrom manganates were also interpreted as the same monoclinic crystal system with beta=90-94 degrees. The unit cell parameters, especially a, c and beta change possibly with the type of substituent cation probably because of the different ionic radius, hydration energy and molar ratio of substituent cation to manganese. However, these diffraction data, except for those of Sr and Ba 7 angstrom and Ca and Ni 10 angstrom manganates, reveal only some parts of the host manganese structure with the edge-shared [MnO6] octahedral layer. On the other hand, one of the superlattice reflections observed in the electron diffractions was found in the X-ray diffraction lines for heavier divalent cations Sr and Ba 7 angstrom and Ca and Ni 10 angtrom manganates. The reflection presumably results from the substituent cation position in the interlayer which is associated with the vacancies in the edge-shared [MnO6] layer and indicates that the essential vacancies are linearly arranged parallel to the b-axis. Furthermore, the characteristic superlattice reflection patterns for several cations, Li, Mg, Ca, Sr, Ba and Ni, manganates were interpreted that the substituent cations are regularly distributed in the interlayer according to the exchange percentage of substituent cation to Na+. In contrast, the streaking in the a-direction observed strongly in the electron diffractions for heavier monovalent cations, K and Cs, manganates probably results from the disordering of their cations in the a-direction in the interlayer.