Micron-scale positioning of features influences the rate of polymorphonuclear leukocyte migration

Microfabrication technology was used to create regular arrays of micron-size holes (2 microm x 2 microm x 210 nm) on fused quartz and photosensitive polyimide surfaces. The patterned surfaces, which possessed a basic structural element of a three-dimensional (3-D) network (i.e., spatially separated mechanical edges), were used as a model system for studying the effect of substrate microgeometry on neutrophil migration. The edge-to-edge spacing between features was systematically varied from 6 microm to 14 microm with an increment of 2 microm. In addition, collagen was used to coat the patterned quartz surfaces in an attempt to change the adhesive properties of the surfaces. A radial flow detachment assay revealed that cell adhesion was the strongest on the quartz surface (approximately 50% cell attached), whereas it was relatively weaker on polyimide and collagen-coated quartz (approximately 25% cell attached). Cell adhesion to each substrate was not affected either by the presence of holes or by the spacing between holes. A direct visualization assay showed that neutrophil migration on each patterned surface could be characterized as a persistent random walk; the dependence of the random motility coefficient (mu) as a function of spacing was biphasic with the optimal spacing at approximately 10 microm on each substrate. The presence of evenly distributed holes at the optimal spacing of 10 microm enhanced mu by a factor of 2 on polyimide, a factor of 2.5 on collagen-coated quartz, and a factor of 10 on uncoated quartz. The biphasic dependence on the mechanical edges of neutrophil migration on 2-D patterned substrate was strikingly similar to that previously observed during neutrophil migration within 3-D networks, suggesting that microfabricated materials provide relevant models of 3-D structures with precisely defined physical characteristics. In addition, our results demonstrate that the microgeometry of a substrate, when considered separately from adhesion, can play a significant role in cell migration.