Hydrothermal Synthesis and Structure of a Potassium Tantalum Defect Pyrochlore
Related Experiment Video
Updated: Oct 3, 2026
Chemical Synthesis of Porous Barium Titanate Thin Film and Thermal Stabilization of Ferroelectric Phase by Porosity-Induced Strain
Published on: March 27, 2018
Niangao Duan1, Zheng-Rong Tian, William S. Willis
1Institute of Materials Science, University of Connecticut, Storrs, Connecticut 06269-3060, U-60, Charles E. Waring Laboratory, Department of Chemistry, University of Connecticut, Storrs, Connecticut 06269-4060, Department of Chemical Engineering, University of Connecticut, Storrs, Connecticut 06269-4060, and Molecular Simulations, Inc., 9685 Scranton Road, San Diego, California 92121-3752.
Abstract:
The synthesis and crystal structure of potassium tantalate (KTa(2)(O,OH)(6).1.8H(2)O) with a defect pyrochlore structure are reported. The compound was crystallized directly from tantalum pentoxide in basic solution under hydrothermal conditions at temperatures as low as 200 degrees C. Ion exchange of this substance in acid yielded an H-type defect pyrochlore. Both highly crystalline K-type and H-type materials absorb argon and have BET surface areas of about 14 m(2)/g. The crystal structures were refined by the Rietveld least-squares method from powder X-ray diffraction data. The final R(wp) and chi(2) were 7.70% and 2.79, respectively. The high thermal stability and control of acidity of these materials, along with the simple and cheap synthesis, may find many applications in sorption, catalysis, and microelectronics.
Related Concept Videos
01:26Imperfections in Crystal Structure: Stoichiometric Point Defects
01:29Imperfections in Crystal Structure: Non-Stoichiometric Defects
01:25Imperfections in Crystal Structure: Point, Line and Plane Defects
02:46Crystal Field Theory - Tetrahedral and Square Planar Complexes
Crystal field theory (CFT) is applicable to molecules in geometries other than octahedral. In octahedral complexes, the lobes of the dx2−y2 and dz2 orbitals point directly at the ligands. For tetrahedral complexes, the d orbitals remain in place, but with only four ligands located between the axes. None of the orbitals points directly at the tetrahedral ligands. However, the dx2−y2 and dz2 orbitals (along the Cartesian axes) overlap with the ligands less than the dxy,...
02:42Valence Bond Theory
02:42Ionic Crystal Structures
Most monatomic ions behave as charged spheres, and their attraction for ions of opposite charge is the same in every direction. Consequently, stable structures for ionic compounds result (1) when ions of one charge are surrounded by as many ions as possible of the opposite...