Thermal evolution of the Cl(-)-LiAl(2) layered double hydroxide: a multinuclear MAS NMR and XRD perspective

Layered double hydroxides (LDHs) with a cation composition of LiAl(2) have a wide range of potential applications as catalysts, catalyst supports, and precursors for refractory oxide materials, including several industrially important lithium aluminate phases. The understanding of the calcination behavior of this group of LDH phases is essential to advancing these applications, and the research described here focuses on the thermal decomposition and structural evolution of LiAl(2)(OH)(6)Cl.nH(2)O in the temperature range of 20-1100 degrees C. (27)Al, (35)Cl, and (6,7)Li magic angle spinning nuclear magnetic resonance spectroscopy, powder X-ray diffraction, thermal analysis (including thermogravimetric and differential scanning calorimetry), and compositional analysis provide a highly consistent picture of the thermally induced phase formation and transformations of this LDH. The loss of the surface and interlayer water can begin as low as room temperature, depending on the relative humidity. Beginning at about 300 degrees C, the simultaneous volatilization of H(2)O and HCl and the exsolution of crystalline LiCl result in the formation of amorphous Li-Al-O-OH. By at least 500 degrees C, volumes with the structures of alpha-LiAlO(2) and LiAl(5)O(8) appear, and these phases become progressively more ordered with increasing temperature. LiCl begins to volatilize by 850 degrees C and is present only in trace amounts above ca. 1000 degrees C. alpha-LiAlO(2) converts to gamma-LiAlO(2) between 970 and 1100 degrees C. Because of the delithiation due to LiCl volatilization, the final products are dominated by LiAl(5)O(8), in contrast to the calcination products of previously studied LiAl(2) LDHs which are dominated by LiAlO(2).