Ni/Pt(111) bimetallic surfaces: unique chemistry at monolayer ni coverage

We have utilized the dehydrogenation and hydrogenation of cyclohexene as probe reactions to compare the chemical reactivity of Ni overlayers that are grown epitaxially on a Pt(111) surface. The reaction pathways of cyclohexene were investigated using temperature-programmed desorption, high-resolution electron energy loss (HREELS), and near edge X-ray absorption fine structure (NEXAFS) spectroscopy. Our results provide conclusive spectroscopic evidence that the adsorption and subsequent reactions of cyclohexene are unique on the monolayer Ni surface as compared to those on the clean Pt(111) surface or the thick Ni(111) film. HREELS and NEXAFS studies show that cyclohexene is weakly pi-bonded on monolayer Ni/Pt(111) but di-sigma-bonded to Pt(111) and Ni(111). In addition, a new hydrogenation pathway is detected on the monolayer Ni surface at temperatures as low as 245 K. By exposing the monolayer Ni/Pt(111) surface to D2 prior to the adsorption of cyclohexene, the total yield of the normal and deuterated cyclohexanes increases by approximately 5-fold. Furthermore, the reaction pathway for the complete decomposition of cyclohexene to atomic carbon and hydrogen, which has a selectivity of 69% on the thick Ni(111) film, is nearly negligible (<2%) on the monolayer Ni surface. Overall, the unique chemistry of the monolayer Ni/Pt(111) surface can be explained by the weaker interaction between adsorbates and the monolayer Ni film. These results also point out the possibility of manipulating the chemical properties of metals by controlling the overlayer thickness.