Study of the composition of tars produced from blends of coal and polyethylene wastes using high-performance liquid...

Tars produced at semi-industrial scale in a coke oven of 6 x 10(3) kg capacity were used to investigate the effect of using polyethylene waste as an additive in the carbonization process with coal. The polyethylene wastes used were low-density polyethylene from the agriculture greenhouses and high-density polyethylene from domestic sources. The high-performance liquid chromatography analysis of the soluble fractions in toluene and carbon disulfide, using two polystyrene-divinylbenzene columns and a mixture of dichloromethane-methanol as a mobile phase, provides useful information on the composition of tars and their derived pitches in terms of the substitution and molecular topology of polynuclear aromatic compounds (PACs). Differences in composition of tars produced with polyethylene waste at 1% (w/w) have been found to be negligible, while a higher amount of the waste (3%, w/w) promoted the formation of peri-condensed PACs at the expense of the substituted cata-condensed PACs. This behaviour is due to more extensive secondary reactions of tar precursors via dealkylation and aromatic condensation taking place during the carbonization process as a consequence of a more viscous co-carbonizing system. Changes in tar composition caused by this amount of polyethylene waste addition were comparable to those promoted by an increase in the carbonization temperature at semi-industrial and industrial ovens and by the coal preheating before the carbonization process. The characteristic features in tar composition were also found for the derived pitches from tars obtained with the polyethylene waste addition.