Characterization of powder components of commercial bone cements

Y Imai1, A Ohyama

  • 1Institute of Biomaterials and Bioengineering, Tokyo Medical and Dental University, 2-3-10, Kanda-Surugadai, Chiyoda-ku, Tokyo 101-0062, Japan.

Dental Materials Journal
|March 28, 2002
PubMed

More Related Videos

Ceramic Omnidirectional Bioprinting in Cell-Laden Suspensions for the Generation of Bone Analogs10:19

Ceramic Omnidirectional Bioprinting in Cell-Laden Suspensions for the Generation of Bone Analogs

Published on: August 8, 2022

Comprehensive Characterization of Tissue Mineralization in an Ex Vivo Model07:29

Comprehensive Characterization of Tissue Mineralization in an Ex Vivo Model

Published on: September 27, 2024

Related Concept Videos

Mortar01:29

Mortar

Mortar, a mixture of Portland cement, hydrated lime, sand, and water, is a crucial binding material in construction. Its primary function is to join masonry units together, filling gaps and ensuring a uniform distribution of weight across the structure. This helps in preventing potential weaknesses. Mortar also serves as a protective barrier against environmental elements such as water and wind, thereby safeguarding the interior of the structure. It also compensates for surface irregularities...
Portland Cement01:21

Portland Cement

Portland cement is the essential binding ingredient in concrete, made from finely ground materials including lime, iron, silica, and alumina. Lime is derived primarily from limestone, marble, marl, seashells, and clays, which also supply iron and alumina, while silica is sourced from sand, chalk, and bauxite. Contemporary manufacturing of Portland cement is a significant source of carbon dioxide emissions, prompting research into reducing its content in concrete through alternative...
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...