Influence of polymerization conditions on monomer elution and microhardness of autopolymerized polymethyl

Shyh-yuan Lee1, Yu-lin Lai, Tzai-shin Hsu

  • 1Faculty of Dentistry, National Yang-Ming University, Taipei, Taiwan. sylee@ym.edu.tw

European Journal of Oral Sciences
|May 16, 2002
PubMed

More Related Videos

Stereolithographic 3D Printing with Renewable Acrylates08:28

Stereolithographic 3D Printing with Renewable Acrylates

Published on: September 12, 2018

Environmental Dynamic Mechanical Analysis to Predict the Softening Behavior of Neural Implants06:59

Environmental Dynamic Mechanical Analysis to Predict the Softening Behavior of Neural Implants

Published on: March 1, 2019

Related Concept Videos

Polymer Classification: Architecture01:14

Polymer Classification: Architecture

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...
Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
Classification and Mechanical Properties of Synthetic Polymers01:28

Classification and Mechanical Properties of Synthetic Polymers

Synthetic polymers are classified as elastomers, fibers, or plastics based on their crystallinity. Crystallinity, the degree of long-range order in the solid state, influences the mechanical properties (stretching or contracting) of elastomers. Elastomers are flexible polymers that can expand or contract easily upon the application of an external force. They have numerous crosslinks that pull them back into their original shape when stress is removed. Silicones, for instance, are highly elastic...
Determination of Molar Masses of Polymers I01:24

Determination of Molar Masses of Polymers I

Polymerization produces macromolecules with a range of chain lengths due to the random nature of molecular growth processes. As chains form and terminate at different stages, a single polymer sample contains molecules of varying sizes rather than a uniform structure. This variability is described using average molar masses and distribution-related parameters, which together provide a comprehensive understanding of polymer characteristics.The distribution of molar masses plays a critical role in...
Determination of Molar Masses of Polymers II01:27

Determination of Molar Masses of Polymers II

Polymer samples typically consist of macromolecular chains with a distribution of lengths, resulting in a range of molar masses rather than a single discrete value. Conventional descriptors such as the number-average molar mass and weight-average molar mass quantify this distribution but do not fully capture polymer behavior in solution..The viscosity-average molar mass provides a more realistic description of polymer behavior in solution because it accounts for the enhanced contribution of...