Scanning electron microscopy and Fourier transformed infrared spectroscopy analysis of bone removal using Er:YAG and
Katia M Sasaki1, Akira Aoki, Shizuko Ichinose
1Department of Hard Tissue Engineering, Graduate School, Tokyo Medical and Dental University, Japan. sasaki.peri@tmd.ac.jp
Background:
A thorough analysis of laser-ablated bone tissue is required before applying the technique to osseous surgery. In this study, we examine the morphological features and chemical composition of the bone surface after Er:YAG and CO2 lasers ablation.
Methods:
Six Wistar rats were used. An Er:YAG laser was used for ablation at an output energy of 100 mJ/pulse and a pulse rate of 10 Hz (1 W). Continuous CO2 laser irradiation was performed at an output energy of 1 W. Sites drilled using a conventional micromotor were used as controls. Analysis using scanning electron microscopy (SEM) and Fourier transformed infrared (FTIR) spectroscopy was performed.
Results:
Er:YAG laser ablation produced a groove with similar dimensions to that produced by bur drilling, whereas the CO2 laser produced only a charred line with minimal tissue removal. SEM observations revealed that the groove produced by the Er:YAG laser had well-defined edges and a smear layer-free surface with a characteristically rough appearance and with entrapped fibrin-like tissue. The melting and carbonization produced by the CO2 laser were not observed on sites irradiated by the Er:YAG laser. FTIR spectroscopy revealed that the chemical composition of the bone surface after Er:YAG laser ablation was much the same as that following bur drilling. The production of toxic substances that occurred after CO2 laser irradiation was not observed following Er:YAG laser irradiation or bur drilling.
Conclusion:
These results suggest that the use of Er:YAG laser ablation may become an alternative method for oral and periodontal osseous surgery.