In vitro and in vivo tests of hydrothermally synthesised hydroxyapatite coating

High pure and crystalline Hydroxyapatite (HA) coatings on titanium alloy were prepared by hydrothermal synthesis (HS) of plasma-sprayed (PS) precursors from brushite powders (HS-HA). In vitro and in vivo tests were done to evaluate its biological property. The HS-HA coating was compared with the current PS-HA coating. Cultures of the primary osteoblasts on these two HA coatings showed similar cell attachment, proliferation and alkaline phosphatase (ALP) expression. The cell morphology on the coatings was demonstrated by scanning electron microscopy (SEM). The cell spread well at 1 day after seeding culture and the extracellular matrix was secreted after 14 days culture. Histomorphometric analysis was conducted on samples implanted in femoral bone of four dogs for 1 and 3 months, and bone-implant contact percentage was evaluated by light microscopy. The calcium and phosphate distribution on the interface of bone-implant was analysed by SEM and electron dispersive X-ray (EDX) analysis. The results show the osteoconduction of HS-HA coated implants.