Bone tissue engineering: treatment of cranial bone defects in rabbits using self-reinforced poly-L,D-lactide 96/4...

This study is one of a series in which the authors evaluate various absorbable sheets to guide bone regeneration in cranial bone defects. The aim was to evaluate the use of self-reinforced poly-L,D-lactide 96/4 (SR-PLA96) sheets for cranial bone tissue engineering in experimental defects in rabbits. Square defects of 10 x 10 mm were created in the right parietal bone. SR-PLA96 implants (15 x 15 mm) were used to cover these defects in 12 New Zealand White rabbits. Similar defects were created in the left parietal bone, but no sheets were used (controls). The rabbits were killed after 6, 24, or 48 weeks. Histology and histomorphometry were used to evaluate healing of the defects. Defects covered with SR-PLA96 sheets showed more abundant bone formation than control (non-covered) defects. At 6 weeks, the defects were occupied mainly by fibrous tissue. At 24 weeks, healing with bone formation was more obvious in the covered defects. At 48 weeks, bone completely bridged defects covered with SR-PLA96 sheets, and incomplete bridging was seen in non-covered control defects. Hence, bone tissue engineering in experimental cranial bone defects in rabbits can be achieved using SR-PLA96 sheets to guide bone regeneration.