Physical properties and blood compatibility of surface-modified segmented polyurethane by semi-interpenetrating
Nobuyuki Morimoto1, Yasuhiko Iwasaki, Nobuo Nakabayashi
1Institute of Biomaterials and Bioengineering, Tokyo Medical and Dental University, 2-3-10, Kanda-surugadai, Chiyoda-ku, Tokyo 101-0062, Japan.
Abstract:
Segmented polyurethanes, (SPU)s, are widely used in the biomedical fields because of their excellent mechanical property. However, when blood is in contact with the SPU, non-specific biofouling on the SPU occurs which reduces its mechanical property. To obtain novel blood compatible elastomers, the surface of the SPU was modified with 2-methacryloyloxyethyl phosphorylcholine (MPC) by forming a semi-interpenetrating polymer network (semi-IPN). The SPU film modified by MPC polymer with the semi-IPN (MS-IPN film) was prepared by visible light irradiation of the SPU film in which the monomers were diffused. X-ray photoelectron spectroscopy confirmed that the MPC units were exposed on the MS-IPN film surface. The mechanical properties of the MS-IPN film characterized by tensile testing were similar to those of the SPU film. Platelet adhesion on MS-IPN films was also investigated before and after stress loading to determine the effects of the surface modification on the blood compatibility. Many platelets did adhere on the SPU film before and after stress loading. On the other hand, the MS-IPN film prevented platelet adhesion even after repeated stress loading.