Electron spin resonance evaluation of pure CaSO4 and as a phosphor doped with P and Dy

Polycrystalline CaSO4 powder, doped with different elements but mainly rare earths, is one of the most interesting thermoluminescent (TL) materials. Although many electron spin resonance (ESR) analyses have been reported for these materials few studies have been published about the potential of CaSO4 for ESR dosimetry; almost all studies used CaSO4:Dy with a very low Dy concentration as the material for TL measurements. Pure CaSO4 from Merck was used to prepare CaSO4:Dy and CaSO4:P:Dy with different Dy concentrations. Samples were annealed at 600 degrees C for 1 h before irradiation in a Gammacell 220 irradiator with a 60Co gamma source at a dose rate of 100 Gy x min(-1). The ESR spectra of the pure CaSO4 and CaSO4 doped with P and Dy show the lines usually observed with these types of material, with the factor g around 2.036 and an intense line at g = 2.0011 found only in the pure material. This line, probably an axial SO4-, grows linearly with absorbed dose until 1.0 kGy and shows good stability with time. The line should be stabilized by matrix impurities because it can be removed by a simple treatment with hot sulphuric acid.