Preparation and thermoluminescence properties of aluminium oxide doped with europium

There is little information concerning the use of rare earths as dopants of Al2O3. This paper presents the preparation method and the results of studying the thermoluminescence characteristics of Al2O3:Eu exposed to ultraviolet light. Phosphor powder was obtained by the evaporation method. Optimum dopant concentration was 10% at an evaporation temperature of 700 degrees C. The powder obtained was submitted to thermal treatments at high temperatures in order to stabilise the traps. Diffraction patterns showed amorphous powder up to 500 degrees C; as the temperature was raised crystalline phases of Al2O3 appeared. The photoluminescence spectrum induced by 250 nm UV light exhibited four well defined peaks characteristic of the Eu3+ ion. The glow curve exhibited two peaks at 180 and 350 degrees C. The sensitivity of Al2O3:Eu was 10 times lower than Al2O3:C. The thermoluminescence response was linear from 2.4 to 3000 microJ.cm(-2) of spectral irradiance, and the fading 2% in a month. From these results it can be concluded that Al2O3:Eu has potential as an UV dosemeter.