Effect of heating rate on the responses of CaF2:Cu, CaF2:Tm, CaF2:Dy and CaF2:Mn

Recent development of CaF2:Cu (the most sensitive material for radiation dosimetry) exhibiting a TL glow peak around 270 degrees C similar to that of CaF2:Mn has made it attractive to study the influence of heating rate on the response of CaF2 based TLDs. Influence of heating rate on CaF2:Mn (known to reduce the response with increasing heating rate) was confirmed in view of the reported controversy about other TLDs. Responses of TL glow peaks around 270 degrees C in CaF2:Cu, CaF2:Tm, CaF2:Dy and CaF2:Mn were studied. Except CaF2:Mn, no other CaF2 based TLD exhibited a reduction in response with increasing heating rate. On the contrary, in some cases a small increase (10-15%) was noted with increasing heating rate from 1 degrees Cs(-1) to 50 degrees Cs(-1). The shape and the position of the glow peak and the parameters derived from the shape of the glow curve appear to have no relation to reduction of TL efficiency at higher heating rates. Apart from the increased probability of non-radiative transitions at higher temperatures, the observed effects have been assigned to the effect of heating rate on the migration of charge carriers released during the TL readout.