Thermoluminescence of MgSO4 doped with Eu and P impurities

CaSO4:Eu, MgSO4:Eu and MgSO4:Eu,P phosphors have been prepared and their thermoluminescence (TL) characteristics were studied. A main glow peak due to Eu2+ ions is seen at approximately 146 degrees C and 440 nm and glow peaks at approximately 145 degrees C, approximately 190 degrees C, approximately 260 degrees C and approximately 360 degrees C for 590 nm and 625 nm wavelengths are identified as Eu3+ ion emissions in MgSO4:Eu. Emission spectra in MgSO4:Eu and the MgSO4:Eu,P show that the MgSO4:Eu3+ glow peak at 260 degrees C for 590 nm and 625 nm shifts to 280 degrees C with enhanced intensity while the Eu2+ ion glow peak at 146 degrees C remains but with reduced intensity. The main glow peak at approximately 146 degrees C and 440 nm from Eu2+ ions shows significant difference from the characteristic glow peaks of Eu3+ ions. It is observed that the wavelength of the Eu2+ ion glow peak is inversely proportional to the radius of the cation of the host sulphate in alkaline-earth sulphate phosphors. By contrast the wavelengths of the Eu3+ ion glow peaks remain unchanged in different sulphates. Besides, the glow curve at approximately 146 degrees C obtained using a conventional blue sensitive reader shows simply the first order kinetics. It is concluded that the luminescence centres and distribution of traps related to Eu2+ ions are different from that of Eu3+ ions in MgSO4:Eu and MgSO4:Eu,P phosphors.