Wettability, imbibition, and mass change of disinfected low-viscosity impression materials
Xavier Lepe1, Glen H Johnson, John C Berg
1Department of Restorative Dentistry, University of Washington, Seattle, Wash 98195-7456, USA. xlepe@u.washington.edu
Statement Of Problem:
There is an ongoing effort by dental manufacturers to create impression materials with improved wetting properties. Disinfection solutions may alter the surface characteristics of these newer materials.
Purpose:
This study compared wettability, imbibition, and mass change of various recently introduced automixed low-viscosity addition silicone and polyether materials before and after immersion disinfection.
Material And Methods:
The Wilhelmy technique was used for deriving wetting properties of 5 addition silicone materials (Clinician's Choice Affinity, Clinician's Choice Superhydrophilic [experimental], Kerr's Take One, 3M's Imprint II, and Dentsply's Aquasil LV) and 2 polyether materials (ESPE's Permadyne Garant and Impregum Garant). Conditions included a control with no disinfection (0 hours), as well as (1/2) hour of immersion disinfection in a full-strength solution of 2% acid glutaraldehyde disinfectant (Banicide). Weight changes before and after disinfection and weight loss in air were measured over an 18-hour period to detect imbibition and mass change over time. The data were analyzed with a 1-way analysis of variance at alpha=0.05, with n = 3 for advancing (ACA) and receding (RCA) contact angles and n = 2 for imbibition and mass change.
Results:
Statistical significant differences in wettability (P<.001) were found among nondisinfection control groups, as well as among (1/2)-hour disinfection groups. Polyethers were the most wettable materials overall. Impregum Garant polyether demonstrated significantly lower RCA for the control (48.4 degrees) and at (1/2) hour of disinfection (51.8 degrees). The 2 polyethers and Take One lost mass, whereas Aquasil LV gained mass in air; however, all materials exhibited some degree of imbibition during disinfection.
Conclusion:
Within the limitations of this study, the 2 polyether materials tested exhibited significantly lower ACA's and RCA's compared with the 5 addition silicones tested. Imbibition for the 2 polyether materials was significantly higher (P<.001). Polyether materials lost significantly more (0.6% to 0.8%) and Aquasil LV gained significantly more (0.6%) mass in air.