Japanese encephalitis virus vaccine formulations using PLA lamellar and PLG microparticles

Japanese encephalitis virus (JEV)-loaded poly(lactide) (PLA) lamellar and poly(DL-lactide-co-glycolide) (PLG) microparticles were successfully prepared with low molecular weight PLA by the precipitate method and with 6% w/v PLG in the organic phase, 10% w/v PVP and 5% w/v NaCl in the continuous phase, by using a water-in-oil-in-water emulsion/solvent extraction technique, respectively. JEV was entrapped in the PLG microparticles by a solvent extraction technique with trapping efficiencies up to 98%, loading level 5.5% w/w, and mean particle size 3.8 microm. The distribution (%) of JEV on the PLG microparticles surface, outer layer, and core were 11.2, 41.7 and 46.4%, respectively. The cumulative release of JEV had an upper limit of approximately 58% of the JEV load at 24 days. The steady release rate was 1.33 microg JEV/mg microparticles/day of JEV release maintained for 24 days. The corresponding virus loading of the PLA lamellae is approximately 0.78% w/w and the loading efficiency (77.8%), JEV content (7.84 microg/mg), and yield (96.3%), respectively. The distribution (%) of JEV on the microparticles surface, outer layer, and core were 82.1, 13.3 and 2.2%, respectively. The live JEV challenge in mice test, in which mice received one dose of 20 mg JEV-loaded PLG microparticles, 20 mg JEV-loaded PLA lamellar in comparison with JEV or PBS solution, was evaluated after IP immunization of BALB/c mice. The study results show that the greatest survival was observed in the group of mice immunized with 20 mg JEV-loaded PLG microparticles and 20 mg JEV-loaded PLA microparticles group (80%). The JEV incorporation, physicochemical characterization data, and the animal results obtained in this study may be relevant in optimizing the vaccine incorporation and delivery properties of these potential vaccine targeting carriers.