Effects of various thiol molecules added on morphology of dendrimer-gold nanocomposites

Interactions between poly(amidoamine) dendrimer (PAMAM)-gold nanocomposites and alkanethiols and between the former nanocomposites and thiol-modified poly(amidoamine) dendrons in ethyl acetate were investigated by adding alkanethiols, such as 1-propanethiol and 1,3-propanedithiol, and thiol-modified poly(amidoamine) dendrons, generations 0.5 and 2.5 (G0.5-SH and G2.5-SH). The PAMAM dendrimers with surface methyl ester groups used were generations 1.5 and 5.5 (G1.5 and G5.5). The mean particle sizes of PAMAM-gold nanocomposites were about 2.1 for G1.5 and 2.4 nm for G5.5. In both nanocomposite systems where 1-propanethiol and 1,3-propanedithiol were added, the mean particle size was about 4 nm, twice that of the systems where these thiols were not added. Increasing the addition of 1,3-propanedithiol made the average particle size smaller for both nanocomposites systems. To compare with alkanethiol, thiol-modified poly(amidoamine) dendron with a highly branched structure on one side was synthesized. Using G2.5-SH as a protective agent, dendron-gold nanocomposites with mean diameters of 3 to 4 nm were obtained. The difference in particle size was seen only when the combination of PAMAM-gold nanocomposites and thiol-modified dendron was less sterically dense, modified dendron (G0.5-SH). The mechanisms for morphology changes in the dendrimer-gold nanocomposites by the addition of these thiols are discussed.