Holding power of bioabsorbable self-reinforced poly-L/DL-lactide 70/30 tacks and miniscrews in human cadaver bone

Several bioabsorbable internal fixation systems are currently in use in the field of bone surgery. To test the mechanical properties of recently developed amorphous self-reinforced poly-L/DL-lactide [SR-P(L/DL)LA] 70/30 tacks in comparison with commercially available SR-P(L/DL)LA 70/30 (BioSorbFX; Bionx Implants Ltd) miniscrews, SR-P(L/DL)LA miniscrews (length = 6.0 mm, core diameter = 1.5 mm, thread diameter = 2.0 mm) and tacks (length = 5.4 mm, core diameter = 1.5 mm, thread diameter = 2.0 mm) were applied to human cadaveric metatarsal (MT) bones (6 pairs of fourth MT bones and 6 pairs of fifth MT bones from donors who were from 29 to 56 years of age at the time of death). Pullout force was measured using a mechanical testing machine. Forty-eight pullout tests were carried out for each implant type. The Student test, Mann-Whitney test, and Spearman coefficient were used for statistical evaluation. The pullout force of tacks was 135.0 +/- 26.1 N, and that of the miniscrews was 119.3 +/- 26.1 N ( = 0.04, statistically significant difference). Accordingly novel SR-P(L/DL)LA 70/30 tacks have a statistically better pullout strength than the SR-P(L/DL)LA 70/30 miniscrews when tested in cadaver MT bones.