Photorefractive effect in the relaxor ferroelectric material 0.91Pb(Zn1/3Nb2/3)O3-0.09PbTiO3

The photorefractive effect in a nominally undoped 0.91Pb(Zn1/3Nb2/3)O3-0.09PbTiO3 single crystal is measured. We report what is, to our knowledge, the first observation of the photorefractive effect in Pb-based relaxor ferroelectric crystals. The crystal is grown by the flux solution method. Then it is cut into a 2 mm x 4 mm x 8 mm piece and electrically poled along the [111] direction. The coupling constant of the two-wave mixing is 17 cm(-1), and the normalized time constant under 1-W/cm(2) illumination is 12 s at a wave-length of 476 nm. The effective trap density is calculated as 5 x 10(16) cm(-3) from the Debye screening length under the assumption of Kukhtarev's band-transport model. The dominant carrier is identified to be holes from the direction of two-wave mixing energy transfer.