Flexural fatigue behavior of resin composite dental restoratives
Ulrich Lohbauer1, Tina von der Horst, Roland Frankenberger
1Policlinic for Operative Dentistry and Periodontology, University of Erlangen-Nuremberg, Gluckstrasse 11, 91054, Erlangen, Germany. lohbauer@dent.uni-erlangen.de
Objective:
The aim of this study was to evaluate the mechanical properties of resin composite dental restoratives under quasi-static and cyclic loading.
Methods:
Four-point-bending bars of 10 different resin composite materials were manufactured according to ISO standard and stored for two weeks in distilled water. The fracture strength (FS) was measured with the four-point-bending test in an universal testing machine. The flexural fatigue limits (FFL) for 10(5) cycles were determined under equivalent loading. All specimens were tested and fatigued in water at 37 degrees C. The data were analyzed using ANOVA, Weibull statistics of FS and the 'staircase' approach of FFL. Fractographic analysis was performed using SEM.
Results:
The initial flexural strength values for the resin composite materials varied from 55.4 MPa for Solitaire up to 105.2 MPa for Filtek Z250. The mean flexural fatigue limit for 10(5) cycles ranged between 37 and 67% of the initial strength. SEM analysis of the fractured surfaces suggests two kinds of failure mechanisms for initial and fatigue fracture.
Significance:
The fatigue behavior of resin composite materials does not correlate with initial strength values. Materials providing high initial strengths do not obviously reveal the best fatigue resistance. Flexural fatigue measurement of resin composite materials should be viewed as a useful tool to evaluate long term mechanical properties.