Biomechanical and histomorphometric investigations on two morphologically differing titanium surfaces with and
M Fini1, L Savarino, N Nicoli Aldini
1Experimental Surgery Department, Codivilla-Putti Research Institute, Rizzoli Orthopaedic Institute, via di Barbiano 1/10, 40136 Bologna, Italy. milena.fini@ior.it
Abstract:
The influence of fluorohydroxyapatite (FHA) coating and surface roughness of Ti6Al4V implants on bone response was investigated. Uncoated and FHA-coated screws with lower (LR and LR+FHA; Ra: 5.7+/-0.2 microm) and higher (HR and HR+FHA; Ra: 21.8+/-0.9 microm) surface roughness, were inserted into the diaphyses of 8 sheep tibiae. Twelve weeks after implantation, extraction torque and bone-to-implant contact were evaluated. The smoothest surfaces showed an improved extraction torque and significant differences were observed between LR and HR (-24.6%, p<0.0005), LR and HR+FHA (-30.7%, p<0.0005), LR+FHA and HR (-17.4%, p<0.005), and LR+FHA and HR+FHA (-24.0%, p<0.005). The bone-to-implant contact data paralleled the biomechanical data: the smoother the surface, the greater the bone-to-implant contact. Significant (p<0.0005) decreases in bone-to-implant contact were observed between LR+FHA and HR (-24.2%), and between LR+FHA and HR+FHA (-29.2%). The current findings suggest that LR surfaces significantly improve the osteointegration rate of implanted cortical screws independently of the FHA coating.