Environmental assessment of cement/foundry sludge products

This work deals with the environmental assessment of products based on cement and a waste from a cast iron activity. The waste is a foundry sludge from wastewater treatment previously characterized. This industrial waste shows a high water content (62.4%) and a hazardous behavior due to its metallic content mainly Zn (16.5%), together with a low fraction of organic pollutants, mainly phenolic compounds. The feasibility of immobilizing both typs of contaminants was studied using Portland cement as binder at different cement/waste ratios. The parameters of environmental control were the ecotoxicity and mobilization of zinc and phenolic compounds, all determined on the basis of compliance leaching tests. The acid neutralization capacity of the cement/waste products was measured in order to obtain information on their buffering capacity. Experimental results from chemical analysis of leachates led to a non ecotoxic character of cement/waste products Although the metallic ions were mobilized within the cement mattices, the organic matter did not allow the formation of monolithic forms and an efficient immobilization of phenolic compounds. Concerning the acid neutralization capacity, this parameter was shown to depend mainly on the quantity of cement, although a decrease in alkalinity was observed when the amount of water in the cement/waste products increased.