Chitosan: potential use as a bioactive coating for orthopaedic and craniofacial/dental implants

Chitosan is a biopolymer that exhibits osteoconductive, enhanced wound healing and antimicrobial properties which make it attractive for use as a bioactive coating to improve osseointegration of orthopaedic and craniofacial implant devices. Coatings made from 91.2% de-acetylated chitosan were chemically bonded to titanium coupons via silane-glutaraldehyde molecules. The bond strength of the coatings was evaluated in mechanical tensile tests, and their dissolution and cytocompatibility were evaluated in vitro using cell-culture medium and UMR 106 osteoblastic cells, respectively. The results showed that the chitosan coatings were chemically bonded to the titanium substrate and that the bond strengths (1.5-1.8 MPa) were not affected by gas sterilization. However, the chitosan bond strengths were less than those reported for calcium-phosphate coatings. The gas-sterilized coatings exhibited little dissolution over 8 weeks in cell-culture solution, and the attachment and growth of the UMR 106 osteoblast cells was greater on the chitosan-coated samples than on the uncoated titanium. These results indicated that chitosan has the potential to be used as a biocompatible, bioactive coating for orthopaedic and craniofacial implant devices.