Mechanical and magnetic properties of nickel-dispersed tetragonal zirconia nanocomposites

Effects of Ni dispersions on microstructure and mechanical properties have been studied for Y2O3-stabilized tetragonal zirconia (Y-TZP)/Ni nanocomposites with Ni dispersion up to 10 vol%. Composites were successfully fabricated by reducing and hot-pressing Y-TZP/NiO powder mixtures. Fracture strength was significantly improved from 1.5 GPa for monolithic Y-TZP to 1.9 GPa for nanocomposites with a small addition of Ni (1-2 vol%). Magnetic properties of Y-TZP/Ni nanocomposites were also investigated. Magnetization curves of Y-TZP/Ni nanocomposites showed typical hysteresis loops of soft magnetic materials, whereas coercivity was much larger than that of pure Ni metal. A new function arising from magnetomechanical effects of metallic Ni is also discussed for the present nanocomposites.