Influence of laminar flow on preorientation of coal tar pitch structural units: Raman microspectroscopic study

In order to estimate the role of laminar flow of viscous, aromatic matter of carbonaceous precursor on microtextural preorientation in pregraphitization stage, we performed experiments with coal tar pitch (CTP). The principal hypothesis of preorientation of basic structural units (BSUs) in the case of laminar flow (pressure impregnation of CTP into porous matrix) and secondary release of volatiles during carbonization were studied. Glass microplates, planar porous medium with average distance between single microplates 5 microm were used as suitable porous matrix. Samples of CTP were carbonized up to 2500 degrees C. Optical microscopy reveals large flow domains in the sample of cokes carbonized between glass microplates. Raman microspectroscopy and high resolution transmission electron microscopy (HRTEM) show that at nanometric scale, the samples do not support the proposed hypotheses. With increasing temperature of pyrolysis, the graphitization of CTP impregnated into porous matrix proceeds to lower degree of structural ordering in comparison with single pyrolyzed CTP. This is explained by the release of volatile matter during carbonization in geometrically restricted spaces. More evident structural changes were discovered with the sample of single coke, where parts of fine grain mosaics, relicts of 'so called QI parts', reveal higher structural organization, in comparison with large and prolonged flow domains, similar to flow domains of cokes from microplates.