[Preparation and spectroscopic properties of terbium polypropenic acid film]

The bonding-type rare earth polymers-polypropenic-acid terbium film was prepared through the bonding way. Three-dimension fluorescence spectra showed that the optimum excitation wavelength was 306 nm, the strongest emission wavelength was 544 nm. The terbium polypropenic-acid film showed the characteristic Tb3+ emission when excited at 306 nm due to 5D4-7FJ transition (J = 6, 5, 4 and 3). The emission maximum at 544 nm was ascribed to 5D4-7F5 transition of Tb3+ and presented strong green emission. The luminescent properties of Tb3+ were not affected by polymerism of propenic-acid and the transparency of polypropenic-acid in visible light region was not affected by the dopping Tb3+. The fluorescence properties and spectroscopic properties of the terbium polypropenic-acid were investigated by excitation spectrum, emission spectrum, IR, far-IR, and Raman spectrum.