Preparation of budesonide and budesonide-PLA microparticles using supercritical fluid precipitation technology

The objective of this study was to prepare and characterize microparticles of budesonide alone and budesonide and polylactic acid (PLA) using supercritical fluid (SCF) technology. A precipitation with a compressed antisolvent (PCA) technique employing supercritical CO2 and a nozzle with 100- microm internal diameter was used to prepare microparticles of budesonide and budesonide-PLA. The effect of various operating variables (temperature and pressure of CO2 and flow rates of drug-polymer solution and/or CO2) and formulation variables (0.25%, 0.5%, and 1% budesonide in methylene chloride) on the morphology and size distribution of the microparticles was determined using scanning electron microscopy. In addition, budesonide-PLA particles were characterized for their surface charge and drug-polymer interactions using a zeta meter and differential scanning calorimetry (DSC), respectively. Furthermore, in vitro budesonide release from budesonide-PLA microparticles was determined at 37 degrees C. Using the PCA process, budesonide and budesonide-PLA microparticles with mean diameters of 1 to 2 microm were prepared. An increase in budesonide concentration (0.25%-1% wt/vol) resulted in budesonide microparticles that were fairly spherical and less agglomerated. In addition, the size of the microparticles increased with an increase in the drug-polymer solution flow rate (1.4-4.7 mL/min) or with a decrease in the CO2 flow rate (50-10 mL/min). Budesonide-PLA microparticles had a drug loading of 7.94%, equivalent to approximately 80% encapsulation efficiency. Budesonide-PLA microparticles had a zeta potential of -37 +/- 4 mV, and DSC studies indicated that SCF processing of budesonide-PLA microparticles resulted in the loss of budesonide crystallinity. Finally, in vitro drug release studies at 37 degrees C indicated 50% budesonide release from the budesonide-PLA microparticles at the end of 28 days. Thus, the PCA process was successful in producing budesonide and budesonide-PLA microparticles. In addition, budesonide-PLA microparticles sustained budesonide release for 4 weeks.