Load dependency and reliability of microhardness measurements on acid-etched enamel surfaces

The load dependency of hardness measurements was investigated on sound and demineralized enamel samples. For all samples investigated, the Knoop hardness number (KHN) varied as a function of the applied load. Higher loads enhanced indenter penetration into the test surface. The variation in KHN values observed in demineralized enamel, both surface-softened and surface-etched, was explained by a decrease in porosity as a function of depth. The reading error for indentations made on surface enamel etched with 37% phosphoric acid gel for 30 s was found to be slightly elevated compared to indentations made on a polished sound enamel surface. It was concluded that the surface microhardness technique can be used for the longitudinal investigation of etched surface enamel.